| Stocks |
|
HIGH SPEED BANDSAW CUTTING FACILITY FOR PROMPT DELIVERY SCHEDULE
BAND SAW SIZE: 1250 X 1500, 1000 X 1250, 450 X 550 mm
STANDARD SIZES AVAILABLE 1.2311 & 1.2738 GRADE
|
| Width |
205 |
255 |
305 |
355 |
410 |
510 |
610 |
810 |
1050 |
1250 |
1500 |
| Thickness |
|
|
|
|
|
|
|
|
|
|
|
| 25 |
|
 |
|
|
|
|
|
|
|
|
|
| 32 |
|
|
|
|
|
|
|
|
|
|
|
| 35 |
|
|
|
|
|
|
|
|
|
|
|
| 40 |
|
|
|
|
|
|
|
|
|
|
|
| 45 |
|
|
|
|
|
|
|
|
|
|
|
| 50 |
|
|
|
|
|
|
|
|
|
|
|
| 55 |
|
|
|
|
|
|
|
|
|
|
|
| 60 |
|
|
|
|
|
|
|
|
|
|
|
| 65 |
|
|
|
|
|
|
|
|
|
|
|
| 75 |
|
|
|
|
|
|
|
|
|
|
|
| 80 |
|
|
|
|
|
|
|
|
|
|
|
| 85 |
|
|
|
|
|
|
|
|
|
|
|
| 90 |
|
|
|
|
|
|
|
|
|
|
|
| 105 |
|
|
|
|
|
|
|
|
|
|
|
| 125 |
|
|
|
|
|
|
|
|
|
|
|
| 135 |
|
|
|
|
|
|
|
|
|
|
|
| 160 |
|
|
|
|
|
|
|
|
|
|
|
| 180 |
|
|
|
|
|
|
|
|
|
|
|
| 205 |
|
|
|
|
|
|
|
|
|
|
|
| 255 |
|
|
|
|
|
|
|
|
|
|
|
| 305 |
|
|
|
|
|
|
|
|
|
|
|
| 335 |
|
|
|
|
|
|
|
|
|
|
|
| 355 |
|
|
|
|
|
|
|
|
|
|
|
| 410 |
|
|
|
|
|
|
|
|
|
|
|
| 460 |
|
|
|
|
|
|
|
|
|
|
|
| 510 |
|
|
|
|
|
|
|
|
|
|
|
| 610 |
|
|
|
|
|
|
|
|
|
|
|
| 710 |
|
|
|
|
|
|
|
|
|
|
|
| 810 |
|
|
|
|
|
|
|
|
|
|
|
| 850 |
|
|
|
|
|
|
|
|
|
|
|
| 910 |
|
|
|
|
|
|
|
|
|
|
|
|
| |
OUR STANDARD QUALITY PROGRAMME FOR MOULD STEELS
All our mould steel grades are melted in furnaces built to the latest technological requirements ensuring the highest degree of metallurgical purity (low sulphur, low hydrogen)
|
| W. -Nr. |
DIN/AISI |
Typical Analysis |
Typical Use |
| 1.0527 |
CK55/AISI 1055 |
C
P + S ea.
Cr |
0,55%
max. 0,035%
0,65% option. |
Base plate, simple mould
NORMAL DELIVERY CONDITION
hardened and tempered, or normalised |
| 1.2311 |
40CrMnMo 7/AISI P20 |
C
Mn
S max.
Cr
Mo |
0,40%
1,45%
0,005%
2,0%
0,20% |
Injection mould of high deformation resistance
and good polishability (F.I. For bottle crates,
t-v housings, frames, fridges doors, buckets etc.)
NORMAL DELIVERY CONDITION:
hardened and tempered to abt. 1000N/mm2 |
| 1.2738 |
40CrMnNiMo 8 6 4/ AISI P20+NI |
C
Mn
S max.
Cr
Mo
Ni |
0,40%
1,50%
0,005%
2,00%
0,20%
1,00% |
Similar to W1.2311, but for bigger diameters,
because of better through - hardening properties,
for cross sections 400 mm and more.
NORMAL DELIVERY CONDITION:
hardened and tempered to 29-34 HRC.
or our variant "high hard" h+t to 35-39 HRC. |
| XPM 36 |
Improved 1.2378 available in
32 - 36 HRC or 36 - 40 HRC |
C
Mn
Cr
Mo
Ni |
0.26
1.50
1.50
0.50
1.10 |
Uniform hardness across the cross-section, very good
polishability, good machinability, greatly increased thermal
conductivity, hardenable and temperable plastic mould steel,
nitridable, suitable for chrome plating and pitting; improve
weldablity as 2738, good toughness
APPLICATIONS: die steel for plastic moulds with a thickness
over 400 mm, moulds for TV housings and rear walls, copier
housings, moulds for dashboards and large outside body parts |
| 1.2343 |
x38CrMoV 5 1 / AISI H 11 |
C
Cr
Mo
v |
0,38%
5,0%
1,1%
0,1% |
Hot work tool steel for tools and dies for metal
forming, pressure casting tool, extruders etc.
NORMAL DELIVERY CONDITION:
Diffusion annealed ("microdized")
with J min. 250, on sample 7 x 10 mm / 45+/ -3 HRC
with J min. 300, on sample 7 x 10 mm / 45+/ -3 HRC |
| 1.2714 |
56NiCrMo V 7 / AISI L6 |
C
Cr
Mo
V |
0,40%
5,10%
1,30%
1,00% |
Hot work tool and die steel for similar applications as
W1.2343, even rougher ones (higher V-content).
NORMAL DELIVERY CONDITION:
Diffusion annealed ("microdized")
with J min. 250, on sample 7 x 10 mm / 45+/ -3 HRC
with J min. 300, on sample 7 x 10 mm / 45+/ -3 HRC |
| 1.2714 |
56NiCrMo V 7 / AISI L6 |
C
Cr
Mo
Ni
V |
0,56%
1,10%
0,50%
1,70%
0,10% |
Tool & die steel mainly for hot forging (Drop -and open)
hot shear blades, extrusion tools, large moulds for the
extrusion of thermoplastics
NORMAL DELIVERY CONDITION:
either: soft annealed to max, 248 HB or: hardened & tem. |
| 1.2316 |
X36CrMo 17 |
C
Cr
Mo |
0,38%
16,00%
1,15% |
This corrosion-resistant steel is used for processing
corrosive plastics. The polishability is very good.
NORMAL DELIVERY CONDITION:
hardened and tempered to 30 - 35 HRC |
| 1.2083 |
X32Cr13 |
C
Cr |
0,42%
13,00% |
For moulds in which synthetic resins are to be processed,
like amino-pasts resp. acetic acid-exuding thermoplasts.
NORMAL DELIVERY CONDITION: annealed. |
|
|
|
|
|
|